Engineering thermoplastics

Reinforced polyamides

15 % carbon fibre and 30 % basalt fibre

AddiNova PA6-15CF

polyamide15 % carbon fibre

A polyamide compound with 15 % carbon fibre for structural 3D printing. Tensile strength of at least 80 MPa, flexural modulus of at least 4900 MPa; the stated operating range is from −60 to 220 °C.

Application per the technical data sheet

Automotive brackets, manifolds and gears; manipulators, drives, bushings and gearboxes; pumps, valves, rollers and guides; motorsport and unmanned aircraft; medical and rehabilitation products*; sports equipment.

Property	Test result
Tensile strength at break, MPa, at least	80
Elongation at break, %, at least	6
Unnotched Charpy impact strength, kJ/m², at least	6
Flexural modulus, MPa, at least	4900
Melt flow rate at 270 °C and 2.16 kg, g/10 min	13
Fibre content, %	15
Shrinkage, %, at most	0.4
Operating temperature range, °C	from −60 to 220

AddiNova PA6-30BF

polyamide 630 % basalt fibre

A compound based on polyamide 6 with 30 % basalt fibre. The grade combines a tensile strength of at least 90 MPa, a flexural modulus of at least 5000 MPa and an unnotched Charpy impact strength of at least 10 kJ/m².

Application per the technical data sheet

Automotive brackets, manifolds and gears; manipulator links, drives, bushings and gearboxes; pumps, valves, rollers and guides; motorsport and unmanned aircraft; medical and rehabilitation products*; sports equipment.

Property	Test result
Tensile strength at break, MPa, at least	90
Elongation at break, %, at least	4
Unnotched Charpy impact strength, kJ/m², at least	10
Flexural modulus, MPa, at least	5000
Fibre content, %	30
Shrinkage, %, at most	0.4
Operating temperature range, °C	from −60 to 220

Advanced materials for additive manufacturing

Request a technical selection.

Specify the process and printer, the function of the part, load, temperature and environment, your current material, the reason for replacing it, the acceptance criterion, volume and country of use.