Engineering thermoplastics

Reinforced ABS grades

15 % basalt fibre and 30 % carbon fibre

AddiNova ABS-15BF

ABS plastic15 % basalt fibre

An ABS-based compound with 15 % basalt fibre. The material is intended for rigid structural parts: flexural modulus of at least 5000 MPa, shrinkage of no more than 0.4 %.

Application per the technical data sheet

Housings of unmanned aircraft and equipment mounts; robotic grippers, gearboxes, gears and tooling; motorsport elements; sports prototypes; electronics housings; rehabilitation and medical products*.

Property	Test result
Tensile strength at break, MPa, at least	55
Elongation at break, %, at least	2
Flexural modulus, MPa, at least	5000
Izod impact strength, J/m²	20
Fibre content, %	15
Shrinkage, %, at most	0.4
Operating temperature range, °C	from −60 to 90

AddiNova ABS-30CF

ABS plastic30 % carbon fibre

A highly filled ABS-based compound with 30 % carbon fibre. According to the technical data sheet, tensile strength at break is at least 120 MPa, compressive strength at least 140 MPa and flexural modulus at least 16,000 MPa.

Application per the technical data sheet

Housings of unmanned aircraft and equipment mounts; robotic grippers, drive housings, gears, casings and tooling; motorsport elements; sports prototypes; electronics housings; rehabilitation and medical products*.

Property	Test result
Tensile strength at break, MPa, at least	120
Elongation at break, %, at least	1
Flexural strength, MPa, at least	130
Compressive strength, MPa, at least	140
Flexural modulus, MPa, at least	16,000
Unnotched Izod impact strength, J/m²	30
Carbon fibre content, %	30
Shrinkage, %, at most	0.4
Operating temperature range, °C	from −40 to 100

Advanced materials for additive manufacturing

Request a technical selection.

Specify the process and printer, the function of the part, load, temperature and environment, your current material, the reason for replacing it, the acceptance criterion, volume and country of use.